ASTALAC™ ABS M140    
    
丙烯腈丁二烯苯乙烯    
    
Marplex Australia Pty. Ltd.   
     
 Technical Data    
     

产品说明

ASTALAC™ ABS M140 is a high heat profile extrusion grade of ABS and is designed for profile extrusion applications requiring a balance of high heat resistance, high toughness and abuse resistance, product rigidity and processability. Typical profile extrusion applications include electro deposition bath metal sheet racking supports and domestic/industrial window frame linings.

Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS M140UV ].

总体

材料状态 • 已商用：当前有效   
资料 1 •  Technical Datasheet (English)
  
搜索 UL 黄卡 •  Marplex Australia Pty. Ltd.
  
 •  ASTALAC™
  
    
供货地区 • 北美洲 • 南美洲 • 亚太地区 
性能特点 • 超高韧性 • 耐热性，高  
 • 可加工性，良好 • 中等硬度  
    
用途 • 型材   
加工方法 • 型材挤出成型   

物理性能  额定值单位制 测试方法
比重  1.04g/cm³ ASTM D792
熔流率 (220°C/10.0 kg) 3.0g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度 3 (3.20 mm) 44.0MPa ASTM D638
伸长率 3 (断裂, 3.20 mm) 45% ASTM D638
弯曲模量 4 (3.20 mm) 2300MPa ASTM D790
弯曲强度 4 (3.20 mm) 76.0MPa ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 280J/m ASTM D256
落锤冲击 (3.20 mm) 20.0J ASTM D3029
硬度  额定值单位制 测试方法
洛氏硬度 (R 计秤) 102 ASTM D785
热性能  额定值单位制 测试方法
热变形温度  ASTM D648
1.8 MPa, 未退火, 3.20 mm 89.0°C 
1.8 MPa, 未退火, 6.40 mm 95.0°C 
1.8 MPa, 未退火, 12.7 mm 102°C 
维卡软化温度 116°C ASTM D1525 5
线形膨胀系数 - 流动 0.000085cm/cm/°C ASTM D696
可燃性  额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
热灯丝点火温度 (1.60 mm) 550°C AS/NZS 60695.2.12
   
注射  额定值单位制 
干燥温度  85.0 到 90.0°C 
干燥时间  3.0 到 6.0hr 
加工（熔体）温度 200 到 240°C 
背压  10.0 到 25.0MPa 
挤出  额定值单位制 
第1气缸区温度 180 到 200°C 
第2气缸区温度 185 到 210°C 

 
 
 
 
 
 
 
ASTALAC™ ABS M140      
丙烯腈丁二烯苯乙烯      
      
Marplex Australia Pty. Ltd.   
      
  挤出  额定值单位制 
     
  第3气缸区温度 190 到 215°C 
  第4气缸区温度 195 到 220°C 
  第5气缸区温度 200 到 230°C 
  模具温度 200 到 230°C 
  牵引辊 75.0 到 105°C