Lustran® ABS LGM

丙烯腈丁二烯苯乙烯

 

INEOS ABS (USA)

 

Technical Data

 

产品说明

 

Lustran ABS LGM is a low-gloss, easy-flow grade of ABS (Acrylonitrile Butadiene Styrene). This general-purpose injection molding grade offers an excellent balance of rigidity, impact strength, and abuse resistance.

 

Lustran ABS LGM resin is designed for applications requiring stringent physical properties and a high-tech, low-gloss appearance. Typical applications include power tool housings; lawn and garden equipment; telecommunications equipment; and business machine applications, such as keyboard housings, keypads, and keycaps. As with any product, use of Lustran ABS LGM resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

UL 黄卡 2 •  E44741-235659

搜索 UL 黄卡 •  INEOS ABS (USA)

•  Lustran® ABS

供货地区 • 北美洲

特性 • 刚性，高 • 抗撞击性，良好 • 通用

• 光泽，低 • 良好的流动性

用途 • 草坪和园林设备 • 商务设备 • 外壳

• 动力/其它工具 • 通讯器材

机构评级 • EC 1907/2006 (REACH)

形式 • 粒子

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.05g/cm³ ASTM D792

特定体积 0.950cm³/g ASTM D792

熔流率（熔体流动速率） ASTM D1238

220°C/10.0 kg 21g/10 min

230°C/3.8 kg 7.0g/10 min

收缩率 - 流动 0.40 到 0.70% ASTM D955

机械性能 额定值单位制 测试方法

拉伸模量 2210MPa ASTM D638

抗张强度 (屈服) 35.9MPa ASTM D638

弯曲模量 2480MPa ASTM D790

弯曲强度 (屈服) 72.4MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (23°C, 3.18 mm) 170J/m ASTM D256

硬度 额定值单位制 测试方法

洛氏硬度 (R 级) 105 ASTM D785

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火, 3.18 mm 88.9°C

0.45 MPa, 未退火, 12.7 mm 92.2°C

0.45 MPa, 退火, 3.18 mm 100°C

0.45 MPa, 退火, 12.7 mm 102°C

1.8 MPa, 未退火, 3.18 mm 75.6°C

1.8 MPa, 未退火, 12.7 mm 87.2°C

1.8 MPa, 退火, 3.18 mm 95.0°C

1.8 MPa, 退火, 12.7 mm 100°C

维卡软化温度 106°C ASTM D1525 4

线形热膨胀系数 - 流动 (-30 到 30°C) 9.0E-5cm/cm/°C ASTM D696

 

 

Lustran® ABS LGM

丙烯腈丁二烯苯乙烯

INEOS ABS (USA)

热性能 额定值单位制 测试方法

RTI Elec (1.57 mm) 60.0°C UL 746

RTI Imp (1.57 mm) 60.0°C UL 746

RTI (1.57 mm) 60.0°C UL 746

可燃性 额定值单位制 测试方法

UL 阻燃等级 UL 94

1.57 mm HB

3.18 mm HB

注射 额定值单位制

干燥温度

A 82.2 到 87.8°C

B 71.1 到 76.7°C

干燥时间

A 2.0hr

B 4.0hr

建议的最大水分含量 < 0.10%

建议注射量 50 到 75%

建议的最大回制料比例 20%

料筒后部温度 235 到 249°C

料筒中部温度 241 到 254°C

料筒前部温度 246 到 260°C

射嘴温度 246 到 260°C

加工（熔体）温度 246 到 266°C

模具温度 43.3 到 65.6°C

注塑压力 68.9 到 110MPa

注射速度 快速

背压 0.345 到 0.689MPa

锁模力 2.8 到 5.5kN/cm²

垫层 < 6.35mm

螺杆长径比 20.0:1.0

螺杆压缩比 2.5:1.0

注射说明

Hold Pressure: 50 - 75% of Injection Pressure

Screw Speed: Moderate

 

 

 

 

 

 