INEOS ABS (USA)

 

Technical Data

 

产品说明

 

Lustran ABS LK197 resin is a high-gloss, medium-impact extrusion grade of ABS (Acrylonitrile Butadiene Styrene). It provides a superior balance between rigidity and impact strength, as well as excellent melt strength for good thermoformability. It is easy to color with ABS color concentrates.

 

Lustran ABS LK197 resin is used for applications that require high gloss and higher rigidity, such as bathtubs, sinks, and shower surrounds for recreational vehicles, and interior liners for ice chests and picnic coolers. As with any product, use of Lustran ABS LK197 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

UL 黄卡 2 •  E44741-235639

搜索 UL 黄卡 •  INEOS ABS (USA)

•  Lustran® ABS

供货地区 • 北美洲

特性 • 刚性，高 • 良好的熔体强度 • 中等抗撞击性

• 高光 • 良好的着色性

用途 • 衬里 • 体育用品

• 建筑应用领域 • 浴室配件

机构评级 • EC 1907/2006 (REACH)

形式 • 粒子

加工方法 • 挤出

物理性能 额定值单位制 测试方法

比重 1.06g/cm³ ASTM D792

特定体积 0.940cm³/g ASTM D792

熔流率（熔体流动速率） (230°C/10.0 kg) 9.2g/10 min ASTM D1238

吸水率 4 (23°C, 24 hr) 0.40% ASTM D570

机械性能 额定值单位制 测试方法

拉伸模量 ASTM D638

-18°C 2550MPa

23°C 2280MPa

71°C 1520MPa

抗张强度 ASTM D638

屈服, -18°C 59.3MPa

屈服, 23°C 40.0MPa

屈服, 71°C 22.1MPa

弯曲模量 ASTM D790

-40°C 2760MPa

23°C 2480MPa

71°C 1930MPa

弯曲强度 ASTM D790

屈服, -40°C 114MPa

屈服, 23°C 63.4MPa

屈服, 71°C 49.6MPa

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 ASTM D256

-40°C, 3.18 mm 91J/m

-18°C, 3.18 mm 130J/m

23°C, 3.18 mm 240J/m

 

 

Lustran® ABS LK197

丙烯腈丁二烯苯乙烯

INEOS ABS (USA)

冲击性能 额定值单位制 测试方法

装有测量仪表的落镖冲击 5, 6 ASTM D3763

-40°C, Peak Energy 10.8J

-40°C, Total Energy 13.6J

-18°C, Peak Energy 19.0J

-18°C, Total Energy 24.4J

23°C, Peak Energy 21.7J

23°C, Total Energy 29.8J

硬度 额定值单位制 测试方法

洛氏硬度 (R 级) 113 ASTM D785

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火 92.8°C

0.45 MPa, 退火 101°C

1.8 MPa, 未退火 85.0°C

1.8 MPa, 退火 93.9°C

线形热膨胀系数 - 流动 9.0E-5cm/cm/°C ASTM D696

RTI Elec (1.47 mm) 60.0°C UL 746

RTI Imp (1.47 mm) 60.0°C UL 746

RTI (1.47 mm) 60.0°C UL 746

可燃性 额定值单位制 测试方法

燃烧速率 4 (3.18 mm) 36mm/min SAE J1685

UL 阻燃等级 (1.47 mm) HB UL 94

光学性能 额定值单位制 测试方法

Gardner光泽度 (60°, 挤压薄板) 90 ASTM D523

挤出 额定值单位制

干燥温度 82.2 到 93.3°C

干燥时间 3.0 到 4.0hr

建议的最大水分含量 < 0.030%

料筒1区温度 216 到 241°C

料筒2区温度 216 到 241°C

料筒3区温度 216 到 241°C

料筒4区温度 216 到 241°C

料筒5区温度 216 到 241°C

熔体温度 216 到 249°C

口模温度 210 到 241°C

牵引辊 62.8 到 104°C

挤压说明

Compression Ratio: 2.5: to 2.7:1

Pump Ratio: 1.5 to 2.0

Max Regrind Allowed: 40%

 

 

 

 

 

 

 