丙烯腈丁二烯苯乙烯

 

INEOS ABS (USA)

 

Technical Data

 

产品说明

 

Lustran ABS 752 resin is a high-gloss, high-impact extrusion grade of ABS (Acrylonitrile Butadiene Styrene). In its natural color (000000), Lustran ABS 752 meets FDA requirements for food contact.** It also provides a superior balance between rigidity and impact strength, as well as excellent melt strength for good thermoformability. It is easy to color with ABS color concentrates.

 

Lustran ABS 752 resin is used for extrusion applications that require high-impact toughness. Typical applications include various carrying cases, table tops, wall panels, and profiles. It is also used as a substrate under other specialty grades, such as Lustran ABS 556 low-gloss resin. As with any product, use of Lustran ABS 752 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

 

UL 黄卡 2 •  E44741-235634

 

搜索 UL 黄卡 •  INEOS ABS (USA)

 

•  Lustran® ABS

 

 

 

供货地区

 

特性

 

用途

 

机构评级

 

外观

 

形式

 

加工方法

 

多点数据

 

 

 

• 北美洲

• 刚性，高 • 较高的熔体稳定性 • 良好的着色性

• 高光 • 抗撞击性，高 • 韧性良好

• 家具 • 墙板 • 型材

• EC 1907/2006 (REACH) • FDA 食品接触, 未评级

• 可用颜色 • 自然色

• 粒子

• 挤出 • 热成型 • 型材挤出成型

• Isothermal Stress vs. Strain • Secant Modulus vs. Strain (ISO

(ISO 11403-1) 11403-1)

 

 

物理性能 额定值单位制 测试方法

比重 1.04g/cm³ ASTM D792

特定体积 0.960cm³/g ASTM D792

熔流率（熔体流动速率） ASTM D1238

230°C/10.0 kg 7.7g/10 min

230°C/3.8 kg 1.7g/10 min

吸水率 (23°C, 24 hr) 0.40% ASTM D570

机械性能 额定值单位制 测试方法

拉伸模量 ASTM D638

-18°C 2070MPa

23°C 1860MPa

71°C 1310MPa

抗张强度 ASTM D638

屈服, -18°C 51.0MPa

屈服, 23°C 35.2MPa

屈服, 71°C 19.3MPa

弯曲模量 ASTM D790

-40°C 2410MPa

23°C 1860MPa

71°C 1520MPa

弯曲强度 ASTM D790

屈服, -40°C 89.6MPa

屈服, 23°C 55.2MPa

屈服, 71°C 41.4MPa

 

 

 

Lustran® ABS 752

丙烯腈丁二烯苯乙烯

INEOS ABS (USA)

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 ASTM D256

-40°C, 3.18 mm 180J/m

-18°C, 3.18 mm 240J/m

23°C, 3.18 mm 370J/m

装有测量仪表的落镖冲击 4, 5 ASTM D3763

-40°C, Peak Energy 28.5J

-40°C, 3.18 mm, Total Energy 31.2J

-18°C, Peak Energy 31.2J

-18°C, Total Energy 40.7J

23°C, Peak Energy 27.1J

23°C, Total Energy 46.1J

硬度 额定值单位制 测试方法

洛氏硬度 (R 级) 102 ASTM D785

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火, 3.18 mm 91.1°C

0.45 MPa, 退火, 3.18 mm 98.9°C

1.8 MPa, 未退火, 3.18 mm 83.9°C

1.8 MPa, 退火, 3.18 mm 92.2°C

线形热膨胀系数 - 流动 9.4E-5cm/cm/°C ASTM D696

RTI Elec (0.762 mm) 60.0°C UL 746

RTI Imp (0.762 mm) 60.0°C UL 746

RTI (0.762 mm) 60.0°C UL 746

可燃性 额定值单位制 测试方法

燃烧速率 6 (3.18 mm) 36mm/min ASTM D635

UL 阻燃等级 (1.50 mm) HB UL 94

光学性能 额定值单位制 测试方法

Gardner光泽度 (60°, 挤压薄板) 90 ASTM D523

挤出 额定值单位制

干燥温度 82.2 到 93.3°C

干燥时间 3.0 到 4.0hr

建议的最大水分含量 < 0.030%

料筒1区温度 216 到 241°C

料筒2区温度 218 到 241°C

料筒3区温度 218 到 241°C

料筒4区温度 218 到 241°C

料筒5区温度 218 到 241°C

熔体温度 216 到 249°C

口模温度 210 到 241°C

牵引辊 62.8 到 104°C

挤压说明

Max. Regrind Allowed: 40%

备注

 

 

 